Influence of Repeated Injection Molding processing on Some Mechanical and Thermal Properties of Wood Plastic Composites
Yazarlar (2)
Prof. Dr. Alperen KAYMAKCI Kastamonu Üniversitesi, Türkiye
Prof. Dr. Nadir Ayrılmış İstanbul Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | Bioresources | ||
| Dergi ISSN | 1930-2126 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI | ||
| Makale Dili | İngilizce | Basım Tarihi | 11-2016 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 10-10-2016 |
| Cilt / Sayı / Sayfa | 11 / 4 / 10112–10121 | DOI | 10.15376/BIORES.11.4.10112-10121 |
| Makale Linki | https://doi.org/10.15376/biores.11.4.10112-10121 | ||
| Özet |
| The influence of repeated cycles of injection molding on some mechanical and thermal properties of wood plastic composites (WPCs) was investigated. Pine wood flour (50 wt%) was mixed with HDPE (50 wt%) containing compatibilizing agent (MAPE, 3 wt%) in a co-rotating twinscrew extruder. The test specimens were produced by injection molding from the pellets dried to the moisture content (MC) of 1%. After the mechanical properties of the WPC test specimens were determined, the failed specimens were subsequently pelletized. These pellets were stored and dried for 4 to 6 h until the repeated injection was molded. These processes were repeated seven times. The results revealed that the flexural strength of WPCs increased by about 5.26% from the original granules to the third injection cycle, but further increments in the number of cycles decreased the flexural strength. The tensile strength and tensile … |
| Anahtar Kelimeler |
| Flexural properties | Repeated injection molding | Tensile properties | Thermal properties | WPC |