Özet |
Geopolymer Mortar is a type of mortar manufactured without the addition of cement and, thus, offers specific benefits when compared to ordinary Portland cement (OPC) among which are the environmental advantages due to quite insignificant greenhouse gas emission in the process of production. We examine blended slag (GGBFS), glass powder (GP) and fly ash (FA) alkali activated mortars with steam-cure (SC) and water-cure (WC) techniques in terms of shrinkage. The results reveal that dry shrinkage strains in samples cured with water at 21 C appear far larger than in samples treated with steam-cure. In addition, Geopolymer shrinkage is reduced whereas the amount of fly ash elevates in the slag content of the mix. |
Anahtar Kelimeler |
Makale Türü | Özgün Makale |
Makale Alt Türü | Diğer hakemli uluslarası dergilerde yayınlanan tam makale |
Dergi Adı | International Journal Of Engineering Research And Development |
Dergi ISSN | 2278-067X |
Dergi Tarandığı Indeksler | Google Scholar |
Makale Dili | İngilizce |
Basım Tarihi | 10-2018 |
Cilt No | 14 |
Sayı | 10 |
Sayfalar | 51 / 55 |
Makale Linki | http://www.ijerd.com/paper/vol14-issue10/H14105155.pdf |