| Özet |
| In this study, WCCo-SiC based coatings were produced on the surface of AISI 1050 steel using high velocity oxygen fuel (HVOF) thermal spraying technique. Ni-based powder was used to connect to together WCCo and SiC powders. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the microstructures of WCCo-SiC based coatings. The surface hardness of substrate and coating were measured using a Vickers hardness tester. The XRD results showed that the WCCo-SiC coatings were mainly composed of WC, W 2 C, SiC, Cr 5 B 3 , γ-Ni and Co phases. It was reported that the microstructure and microhardness of coatings generally changed depending on the amount of SiC and WCCo. |
| Anahtar Kelimeler |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | Diğer hakemli uluslarası dergilerde yayınlanan tam makale |
| Dergi Adı | Kastamonu University Journal of Engineering and Sciences |
| Dergi ISSN | 2149-4037 |
| Dergi Tarandığı Indeksler | Index copernicus |
| Makale Dili | Türkçe |
| Basım Tarihi | 06-2015 |
| Cilt No | 1 |
| Sayı | 1 |
| Sayfalar | 1 / 7 |
| Makale Linki | https://dergipark.org.tr/tr/download/article-file/180194 |