Özet |
The effect of Nd2O3 addition on the microstructural and the superconducting properties of Bi-2212 superconductor ceramics, prepared by solid state reaction method, was analyzed by performing X-ray diffraction (XRD), scanning electronic microscope (SEM), energy dispersive spectroscopy (EDS) and dc Resistivity (ρ-T) measurements. The magnetoresistivity of the samples was measured for different values of the applied magnetic field strengths (0-7 T). Also, the activation energies were calculated using the Arrhenius equation. According to these results, the Tcoffset value of the undoped sample was decreased from 79 to 42 K with the growth of magnetic field. In the same way, the activation energy (U o) values were significantly diminished by the increasing of magnetic field. A similar situation was observed in other doped samples. Activation energy for 0.05 % Nd2O3 doped sample under 7 T magnetic field was 550 J/mol the least. In addition, lattice parameter c, calculated by analysis of XRD data, was decreased with doping while lattice parameter a was increased. SEM analysis shows that particles were shrinking with the addition. When compared with other elements for EDS analyses, it was analyzed an important decrease in the percentage of Sr with the increasing of Nd contribution. © Springer Science+Business Media New York 2013. |
Anahtar Kelimeler |
Makale Türü | Özgün Makale |
Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
Dergi Adı | Journal of Materials Science: Materials in Electronics |
Dergi ISSN | 0957-4522 |
Dergi Tarandığı Indeksler | SCI-Expanded |
Makale Dili | İngilizce |
Basım Tarihi | 01-2014 |
Cilt No | 25 |
Sayı | 1 |
Sayfalar | 444 / 453 |
Doi Numarası | 10.1007/s10854-013-1608-1 |
Makale Linki | http://link.springer.com/10.1007/s10854-013-1608-1 |