Effect of Wood Acetylation with Vinyl Acetate and Acetic Anhydride on the Properties of Wood Plastic Composites
Yazarlar (5)
Nilgül Özmen
Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
Nihat Sami Çetin Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
Fatih Mengeloǧlu
Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
Doç. Dr. Emre BİRİNCİ Kastamonu Üniversitesi, Türkiye
Prof. Dr. Kadir Karakuş Kahramanmaras Sütçü Imam Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Bioresources (Q1) | ||
| Dergi ISSN | 1930-2126 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2013 |
| Cilt / Sayı / Sayfa | 8 / 1 / 753–767 | DOI | 10.15376/biores.8.1.753-767 |
| Makale Linki | https://bioresources.cnr.ncsu.edu/resources/effect-of-wood-acetylation-with-vinyl-acetate-and-acetic-anhydride-on-the-properties-of-wood-plastic-composites/ | ||
| UAK Araştırma Alanları |
Odun Mekaniği ve Teknolojisi
|
||
| Özet |
| Chemical modifications of Scots pine (Pinus sylvestris) wood flour were performed with vinyl acetate (VA) and acetic anhydride (AA) in the presence of potassium carbonate as a catalyst. Scots pine wood flour samples were successfully acetylated with VA (19 wt% gain) and AA (24 wt% gain). The effect of chemical modification of the Scots pine wood flour with AA and VA on the mechanical properties of wood high-density polyethylene composites (WPC) was determined. It was observed that acetylation of wood flour allowed a significant increase in both the mechanical properties and the thermal stability of the WPCs. It was concluded that acetylation of lignocellulosic fibers improves thermal stability, dispersion in the polymer matrix, and compatibility with the polymer matrix. |
| Anahtar Kelimeler |
| Acetic anhydrides | Acetylation | Scots pine | Vinyl acetate | Wood plastic composites |
| Atıf Sayıları | |
| Web of Science | 23 |
| Scopus | 25 |
| Google Scholar | 25 |