The Effect of Nd2O3 Addition on Superconducting and Structural Properties and Activation Energy Calculation of Bi 2212 Superconducting System
Yazarlar (7)
Prof. Dr. Özgür ÖZTÜRK Kastamonu Üniversitesi, Türkiye
Doç. Dr. Elif AŞIKUZUN TOKEŞER Kastamonu Üniversitesi, Türkiye
M. Coskunyurek
Kastamonu Üniversitesi, Türkiye
N. Soylu
Bolu Abant İzzet Baysal Üniversitesi, Türkiye
Prof. Dr. Aybaba HANÇERLİOĞULLARI Kastamonu Üniversitesi, Türkiye
A. Varilci
Bolu Abant İzzet Baysal Üniversitesi, Türkiye
C. Terzioglu
Bolu Abant İzzet Baysal Üniversitesi, Türkiye
Makale Türü Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
Dergi Adı Journal of Materials Science Materials in Electronics
Dergi ISSN 0957-4522 Wos Dergi Scopus Dergi
Dergi Tarandığı Indeksler SCI-Expanded
Makale Dili İngilizce Basım Tarihi 03-2014
Cilt / Sayı / Sayfa 25 / 1 / 444–453 DOI 10.1007/s10854-013-1608-1
UAK Araştırma Alanları
Yarı İletkenler
Özet
The effect of Nd2O3 addition on the microstructural and the superconducting properties of Bi-2212 superconductor ceramics, prepared by solid state reaction method, was analyzed by performing X-ray diffraction (XRD), scanning electronic microscope (SEM), energy dispersive spectroscopy (EDS) and dc Resistivity (ρ-T) measurements. The magnetoresistivity of the samples was measured for different values of the applied magnetic field strengths (0-7 T). Also, the activation energies were calculated using the Arrhenius equation. According to these results, the Tc offset value of the undoped sample was decreased from 79 to 42 K with the growth of magnetic field. In the same way, the activation energy (U o) values were significantly diminished by the increasing of magnetic field. A similar situation was observed in other doped samples. Activation energy for 0.05 % Nd2O3 doped sample under 7 T magnetic field was 550 J/mol the least. In addition, lattice parameter c, calculated by analysis of XRD data, was decreased with doping while lattice parameter a was increased. SEM analysis shows that particles were shrinking with the addition. When compared with other elements for EDS analyses, it was analyzed an important decrease in the percentage of Sr with the increasing of Nd contribution. © Springer Science+Business Media New York 2013.
Anahtar Kelimeler
BM Sürdürülebilir Kalkınma Amaçları
Atıf Sayıları
Scopus 8
The Effect of Nd2O3 Addition on Superconducting and Structural Properties and Activation Energy Calculation of Bi 2212 Superconducting System

Paylaş

İletişim
  • Kastamonu Üniversitesi Rektörlüğü, Kuzeykent Kampüsü, Merkez/Kastamonu
  • unis@kastamonu.edu.tr 03662801000
Sosyal Media
Talentsoft Yazılım Talent Yazılım
Tasarım ve Programlama #2025