Prof. Dr. Serkan ISLAK
Kastamonu Üniversitesi, Türkiye |
Dr. Öğr. Üyesi Cihan ÖZORAK
Kastamonu Üniversitesi, Türkiye |
| Özet |
| This study aims to investigate microstructure, hardness, corrosion and wear properties of FeCrNiMo-based coating produced on AISI 1040 steel by using laser welding method. Microstructure properties and phase formation were examined by SEM-EDS and XRD. Thehardness measurement was made by using a microhardness device along a line from the uppersurface of the coating to the substrate. The wear tests of both the substrate and coating layerwere made with a scratch test device. SEM examinations showed that the coating layer had adendritic microstructure and was uniformly bonded to the substrate. The coating layer washarder than the substrate. According to wear tests, the friction coefficient of the coating layerwas lower compared to the substrate. Substrate and coating layer were immersed in an aqueous solution of %3,5 NaCl for potentiodynamic measurements. Corrosion results showedthat coating of the AISI 1040 steel with FeCrNiMo increased the corrosion resistance. |
| Anahtar Kelimeler |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | Ulusal alan endekslerinde (TR Dizin, ULAKBİM) yayımlanan tam makale |
| Dergi Adı | Hittite Journal of Science Engineering |
| Dergi ISSN | 2149-2123 |
| Dergi Tarandığı Indeksler | TR DİZİN |
| Makale Dili | Türkçe |
| Basım Tarihi | 10-2018 |
| Cilt No | 5 |
| Sayı | 3 |
| Sayfalar | 219 / 223 |
| Doi Numarası | 10.17350/HJSE19030000098 |
| Makale Linki | https://www.hjse.hitit.edu.tr/hjse/index.php/HJSE/article/view/HJSE19030000098 |
| Atıf Sayıları | |
| Google Scholar | 3 |