Effects of TiC content on transverse rupture strength TRS of Cu TiC composites produced using powder metallurgy PM technique
Yazarlar (3)
Prof. Dr. Serkan ISLAK Kastamonu Üniversitesi, Türkiye
S. Buytoz Firat Üniversitesi, Türkiye
Dr. Öğr. Üyesi Özkan ESKİ Kastamonu Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Journal of Optoelectronics and Advanced Materials | ||
| Dergi ISSN | 1454-4164 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2015 |
| Cilt / Sayı / Sayfa | 17 / 1 / 211–215 | DOI | – |
| Özet |
| Cu-TiC composites have been produced by powder metallurgy technique. Mixtures of Cu–TiC powders corresponding to weight fractions of 1, 3, 5, 10 and 15 wt.% TiC were hot-pressed for 4 min at 700 C under an applied pressure of 50 MPa. The transverse rupture strength (TRS) of the composites was evaluated by a three-point bending test. SEM were used to analyze the resulting fracture surfaces from the bending test. The TRS decreased rapidly in the 0-5 wt.% TiC contents, while it decreased slowly in the 5-15 wt.% TiC contents. SEM results showed that with the increase in the addition of titanium carbide to copper matrix, pores and gaps were present in the structure.. |
| Anahtar Kelimeler |
| Cu-TiC | Metal matrix composites | Transverse rupture strength |