Experimental and theoretical approaches for magnetic, superconducting and structural characterization of Bi 1.75 Pb 0.25 Sr 2 Ca 2 Cu 3-x Sn x O 10 y glass ceramics
Yazarlar (6)
Prof. Dr. Haluk Koralay Gazi Üniversitesi, Türkiye
Prof. Dr. Sukru Cavdar Gazi Üniversitesi, Türkiye
Aysun Arslan
Gazi Üniversitesi, Türkiye
Gazi Üniversitesi, Türkiye
Prof. Dr. Özgür ÖZTÜRK Kastamonu Üniversitesi, Türkiye
Prof. Dr. Ahmet Tolga TAŞÇI Kastamonu Üniversitesi, Türkiye
Prof. Dr. Nihat Tugluoglu Giresun Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Cryogenics | ||
| Dergi ISSN | 0011-2275 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 12-2017 |
| Cilt / Sayı / Sayfa | 88 / 1 / 17–21 | DOI | 10.1016/j.cryogenics.2017.09.006 |
| Makale Linki | http://linkinghub.elsevier.com/retrieve/pii/S0011227517301960 | ||
| Özet |
| In this work, the effect of the partial substitution of Sn for Cu on structural, electrical and magnetic properties in the superconducting ceramic glass Bi1.75Pb0.25Sr2Ca2Cu3-xSnxO10+y system (x = 0, 0.1, 0.5) has been examined. The structural characterization of samples produced by glass-ceramic technique were done by X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements. The electrical and magnetic properties were determined by resistance-temperature (R-T) measurement and magnetization-magnetic field measurement (M-H) in the low temperature by using vibrating sample magnetometer (VSM), respectively. From the results of R-T measurement, the value of critical temperature (Tcoffset) has been decreased from 98 K to 73 K with increasing Sn- concentration. The critical current density has also been decreased with increasing magnetic field intensity. It has been observed from … |
| Anahtar Kelimeler |
| BSCCO | Glass-ceramic | Superconductivity |
Science Direct
Experimental and theoretical approaches for magnetic, superconducting and structural characterization of Bi 1.75 Pb 0.25 Sr 2 Ca 2 Cu 3-x Sn x O 10 y glass ceramics
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| Web of Science | 6 |
| Scopus | 5 |
| Google Scholar | 7 |