The effects of furnace carbon blacks on the mechanical and the rheological properties of SBR1502 styrene butadiene rubber
Yazarlar (3)
Enver Demirhan
Kocaeli Üniversitesi, Türkiye
Kocaeli Üniversitesi, Türkiye
Prof. Dr. Fatma Kandemirli Kocaeli Üniversitesi, Türkiye
Mithat Kandemirli
Petrochemical Complex, Türkiye
Petrochemical Complex, Türkiye
| Makale Türü | Özgün Makale (Diğer hakemli uluslarası dergilerde yayınlanan tam makale) | ||
| Dergi Adı | Materials and Design | ||
| Dergi ISSN | 0261-3069 | ||
| Makale Dili | İngilizce | Basım Tarihi | 04-2007 |
| Cilt / Sayı / Sayfa | 28 / 4 / 1326–1329 | DOI | 10.1016/j.matdes.2006.01.002 |
| UAK Araştırma Alanları |
|
||
| Özet |
| Thirty-six different compounds were prepared by using SBR1502 type of styrene butadiene rubber and furnace carbon blacks as N220, N326, N330, N347, N550 and N660 according to a standard compounding formulation. The rheological properties of unvulcanized compound were measured, and then mechanical properties of vulcanized compounds as tensile strength, modulus at 300% elongation, elongation at break and hardness value were tested according with ASTM standards. The effect of the furnace carbon blacks on styrene butadiene rubber compound was investigated. The test results were analyzed to determine the suitable furnace carbon black types for styrene butadiene rubber. |
| Anahtar Kelimeler |
Science Direct
The effects of furnace carbon blacks on the mechanical and the rheological properties of SBR1502 styrene butadiene rubber
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| Scopus | 2 |
| Google Scholar | 24 |