Effect of hyamine on electrochemical behaviour of brass alloy in HNO3 solution
Yazarlar (5)
Demet Özkır Niğde Ömer Halisdemir University, Türkiye
Emel Bayol Niğde Ömer Halisdemir University, Türkiye
A. Ali Gürten
Osmaniye Korkut Ata University, Türkiye
Osmaniye Korkut Ata University, Türkiye
Yavuz Sürme Niğde Ömer Halisdemir University, Türkiye
Prof. Dr. Fatma Kandemirli Kastamonu Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Chemical Papers | ||
| Dergi ISSN | 0366-6352 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2013 |
| Cilt / Sayı / Sayfa | 67 / 2 / 202–212 | DOI | 10.2478/s11696-012-0255-y |
| Makale Linki | http://www.degruyter.com/view/j/chempap.2013.67.issue-2/s11696-012-0255-y/s11696-012-0255-y.xml | ||
| UAK Araştırma Alanları |
|
||
| Özet |
| The electrochemical behaviours of a brass alloy in 0.1 M nitric acid, including the hyamine inhibitor with concentrations between 2.5 × 10−4 M and 1.0 × 10−5 M, were studied. For this purpose, potentiodynamic polarisation, electrochemical impedance spectroscopy (EIS), linear polarisation resistance (LPR) techniques, and flame atomic absorption spectroscopy (FAAS) were utilised. The inhibitor molecules adsorbed on the brass surface were calculated to be in good agreement with the Langmuir adsorption isotherm and the standard free enthalpy of adsorption (ΔGads∘). Hyamine effectively improved the corrosion inhibition of brass and acted as a mixed-type inhibitor on alloy surfaces. The surface morphology of the alloy was also clarified by optical microscopic and SEM techniques. A theoretical study of the corrosion inhibition efficiency of hyamine molecule was carried out using density functional theory (DFT) at … |
| Anahtar Kelimeler |
| acid corrosion inhibitor | brass | computational techniques | dezincification | electrochemical techniques |