| Yazarlar |
Doç. Dr. Mehmet AKKAŞ
Kastamonu Üniversitesi, Türkiye |
Prof. Dr. Serkan ISLAK
Kastamonu Üniversitesi, Türkiye |
| Özet |
| In this study, NiB-TiC composite materials were produced using powder metallurgy. In the Ni-TiC-B powder mixture, TiC was fixed at a rate of 5 %, 5, 10 and 15 % boron was added and mechanical alloying was carried out. The prepared powder mixtures were cold pressed under pressure of 400 MPa and sintered in an argon atmosphere at 800oC for 2 hours. Microstructure, phase formation, hardness, wear and corrosion properties of the samples were investigated in detail. Scanning electron microscopy (SEM) was used for microstructure analysis and X-ray diffractogram (XRD) was used for phase formation detection. The hardness measurements of the samples were measured by a microhardness measuring device. Densities of the samples were determined by Archimedes' principle. The corrosion tests were performed potentiodynamic polarization curves of the composite materials in 3.5 % NaCl solution. Wear tests were carried out the composite materials under a load of 10 N. Results showed that by increasing the amount of B, the wear and corrosion resistance increased. |
| Anahtar Kelimeler |
| Corrosion | Mechanical alloying | NiB-TiC composites | Powder metallurgy | Sintering |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | SCIENCE OF SINTERING |
| Dergi ISSN | 0350-820X |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q2 |
| Makale Dili | İngilizce |
| Basım Tarihi | 01-2019 |
| Cilt No | 51 |
| Sayı | 3 |
| Sayfalar | 327 / 338 |
| Doi Numarası | 10.2298/SOS1903327A |
| Makale Linki | http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1903327A |
| Atıf Sayıları | |
| WoS | 13 |
| SCOPUS | 14 |
| Google Scholar | 24 |