WEAR CHARACTERISTICS OF FeW/FeW-B4C COATINGS PRODUCED BY TIG PROCESS      
Yazarlar
Prof. Dr. Serkan ISLAK
Kastamonu Üniversitesi, Türkiye
Özet
In this study, wear properties of FeW-B4C coatings produced by tungsten inert gas (TIG) process on the AISI 1060 steel were investigated. TIG process was selected because it is a cost-effective approach for melting-based coatings. The treated surfaces were evaluated and characterized by means of scanning electron microscope (SEM), X-ray diffraction analysis, and electron dispersive spectrometry (EDS). The microhardness and wear experiment were also performed by using a microhardness machine and ball-on-disk tribometer. SEM observations showed that the obtained coating had a smooth and uniform surface. According to XRD analysis, borides and carbides phases formed in the coatings. The wear behavior of the coatings was compared with ball-on-disc configuration wear tests, at the same conditions. Average coefficient of friction values of the coatings were obtained at relatively low levels.
Anahtar Kelimeler
coating | microstructure | TIG process | Wear
Makale Türü Özgün Makale
Makale Alt Türü SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale
Dergi Adı ARCHIVES OF METALLURGY AND MATERIALS
Dergi ISSN 1733-3490
Dergi Tarandığı Indeksler SCI-Expanded
Makale Dili İngilizce
Basım Tarihi 12-2017
Cilt No 62
Sayı 4
Sayfalar 2001 / 2006
Doi Numarası 10.1515/amm-2017-0298
BM Sürdürülebilir Kalkınma Amaçları
Atıf Sayıları
WoS 2
SCOPUS 2
Google Scholar 4
WEAR CHARACTERISTICS OF FeW/FeW-B4C COATINGS PRODUCED BY TIG PROCESS

Paylaş