Yazarlar |
Prof. Dr. Serkan ISLAK
Kastamonu Üniversitesi, Türkiye |
Özet |
In this study, wear properties of FeW-B4C coatings produced by tungsten inert gas (TIG) process on the AISI 1060 steel were investigated. TIG process was selected because it is a cost-effective approach for melting-based coatings. The treated surfaces were evaluated and characterized by means of scanning electron microscope (SEM), X-ray diffraction analysis, and electron dispersive spectrometry (EDS). The microhardness and wear experiment were also performed by using a microhardness machine and ball-on-disk tribometer. SEM observations showed that the obtained coating had a smooth and uniform surface. According to XRD analysis, borides and carbides phases formed in the coatings. The wear behavior of the coatings was compared with ball-on-disc configuration wear tests, at the same conditions. Average coefficient of friction values of the coatings were obtained at relatively low levels. |
Anahtar Kelimeler |
coating | microstructure | TIG process | Wear |
Makale Türü | Özgün Makale |
Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
Dergi Adı | ARCHIVES OF METALLURGY AND MATERIALS |
Dergi ISSN | 1733-3490 |
Dergi Tarandığı Indeksler | SCI-Expanded |
Makale Dili | İngilizce |
Basım Tarihi | 12-2017 |
Cilt No | 62 |
Sayı | 4 |
Sayfalar | 2001 / 2006 |
Doi Numarası | 10.1515/amm-2017-0298 |