| Özet |
| Cu-TiC composites have been produced by powder metallurgy technique. Mixtures of Cu-TiC powders corresponding to weight fractions of 1, 3, 5, 10 and 15 wt.% TiC were hot-pressed for 4 min at 700 °C under an applied pressure of 50 MPa. The transverse rupture strength (TRS) of the composites was evaluated by a three-point bending test. SEM were used to analyze the resulting fracture surfaces from the bending test. The TRS decreased rapidly in the 0-5 wt.% TiC contents, while it decreased slowly in the 5-15 wt.% TiC contents. SEM results showed that with the increase in the addition of titanium carbide to copper matrix, pores and gaps were present in the structure. |
| Anahtar Kelimeler |
| Cu-TiC | Metal matrix composites | Transverse rupture strength |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS |
| Dergi ISSN | 1454-4164 |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Makale Dili | İngilizce |
| Basım Tarihi | 01-2015 |
| Cilt No | 17 |
| Sayı | 1 |
| Sayfalar | 211 / 215 |