THE EFFECT OF B4C ADDITION ON PORE MORPHOLOGY OF THE ALSI7 FOAMS
Yazarlar (2)
Prof. Dr. Arif UZUN Kastamonu Üniversitesi, Türkiye
Mehmet Turker Gazi Üniversitesi, Türkiye
Makale Türü Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
Dergi Adı Journal of the Faculty of Engineering and Architecture of Gazi University (Q4)
Dergi ISSN 1300-1884 Dergi Bilgileri (2015)
Makale Dili İngilizce Basım Tarihi 01-2015
Cilt / Sayı / Sayfa 30 / 3 / 523–532 DOI –
UAK Araştırma Alanları
Mühendislik
Özet
In this study, the effect of B4C addition on pore morphology of the AlSi7 foams produced via powder metallurgy method was examined. For this, 7 % Si, 1 % TiH2 (foaming agent) and B4C powders at various rates (2, 4 and 6 %) were added to the Al powders and then mixed properly. Mixed powders were compacted at 400 MPa and extruded and rolled to produce precursor material. Then produced samples were freely foamed at temperatures between 690 °C and 750 °C in order to produce closed cell metallic foams. As a result of experimental studies, the volumetric expansion rate of B4C reinforced preform materials has been found to be lower than AlSi7 foams. Expansion values was found to be increase with increasing the foaming temperature. The maximum volumetric expansion values (350 % - 400 %) in nearly all samples was obtained at 750 °C foaming temperature. Pore size and sphericity factor were increased with foaming temperature and the amount of B4C in the samples but they reduced the number of pores.
Anahtar Kelimeler
AlSi7 foam | B4C | Pore morphology | Powder metallurgy
BM Sürdürülebilir Kalkınma Amaçları
Atıf Sayıları
Scopus 1

Paylaş

İletişim
  • Kastamonu Üniversitesi Rektörlüğü, Kuzeykent Kampüsü, Merkez/Kastamonu
  • unis@kastamonu.edu.tr 03662801000
Sosyal Media
Talentsoft Yazılım Talent Yazılım
Tasarım ve Programlama #2025