Analysing the impact of Dy dopants on Zn-based hydroxyapatites: modelling and characterization perspectives
Yazarlar (8)
Oznur Büyük
Firat Üniversitesi Tip Fakültesi, Türkiye
Firat Üniversitesi Tip Fakültesi, Türkiye
Prof. Dr. Nıyazı Bulut Firat Üniversitesi Tip Fakültesi, Türkiye
M. Mursıt Temuz
Firat Üniversitesi Tip Fakültesi, Türkiye
Firat Üniversitesi Tip Fakültesi, Türkiye
Öğr. Gör. Dr. Cahit ÖREK Kastamonu Üniversitesi, Türkiye
Doç. Dr. Tankut Ates Malatya Turgut Ozal University, Türkiye
Prof. Dr. Omer Kaygılı Firat Üniversitesi Tip Fakültesi, Türkiye
İmren Özcan
Inönü Üniversitesi, Türkiye
Inönü Üniversitesi, Türkiye
Alı Kuruçay
Inönü Üniversitesi, Türkiye
Inönü Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Bulletin of Materials Science (Q3) | ||
| Dergi ISSN | 0250-4707 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | Türkçe | Basım Tarihi | 06-2024 |
| Cilt / Sayı / Sayfa | 47 / 3 / 1–14 | DOI | 10.1007/s12034-024-03195-3 |
| Makale Linki | https://doi.org/10.1007/s12034-024-03195-3 | ||
| UAK Araştırma Alanları |
Fiziksel Kimya
Spektroskopi
Teorik Kimya
|
||
| Özet |
| This study is aimed to investigate the effects of introducing dysprosium (Dy) into Zn-based hydroxyapatite (HAp) at various concentrations (0.45, 0.90, 1.35 and 1.80%). The structural and optical properties of pure and doped HAp were thoroughly examined through theoretical and empirical analyses, including X-ray diffraction, Raman spectroscopy and Fourier transform infrared (FTIR) studies. The results confirmed the successful incorporation of Dy into the HAp lattice without significantly affecting its thermal stability or stoichiometry. The introduction of Dy into Zn-based HAp led to notable alterations in several material parameters. The lattice parameters, crystallinity, lattice stress, strain and anisotropic energy density varied with different Dy concentrations. In comparison with undoped HAp, all Dy-doped Zn-based HAps exhibited reduced crystallite size values, indicating a change in the microstructure. Furthermore … |