| Özet |
| In this study, powder metallurgical Cu-Ni-Si alloys with different Ni:Si ratios are produced by cold pressing sintering (600 MPa, at 950°C for 60 min) and bulk materials are solution annealed at 950 °C for 60 min, quenched in water and aged at 450°C for 60 min. A fine distribution of Ni-Si compounds embedded in a netted-free structure is formed in the matrix. Although a conductivity level of at least 22% IACS is achieved in all powder metallurgical alloys, the impurity effect is dominant and a decrease in the conductivity is detected by increasing Ni:Si ratio. However, a slight increase in electrical conductivity is achieved by the precipitation of nickel silicides in the α-Cu matrix under aging conditions. Increasing Ni:Si ratio directly increases the hardness of the powder metallurgical matrix, and a hardness value of 73 HV0.1 is obtained for the aged alloy having the highest Ni:Si (5:1) ratio. |
| Anahtar Kelimeler |
| Conductivity | Corson alloy | Hardness | Powder metallurgy |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | SCIENCE OF SINTERING |
| Dergi ISSN | 0350-820X Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q3 |
| Makale Dili | İngilizce |
| Basım Tarihi | 01-2023 |
| Cilt No | 55 |
| Sayı | 4 |
| Sayfalar | 425 / 436 |
| Doi Numarası | 10.2298/SOS230329026A |
| Makale Linki | http://ojs.itn.sanu.ac.rs/index.php/scisint/issue/view/98 |
| Atıf Sayıları | |
| WoS | 1 |
| SCOPUS | 2 |
| Google Scholar | 3 |