Nano Zirconium Carbide Powder Synthesis via Carbothermal Route
Yazarlar (5)
Dr. Öğr. Üyesi Farzin ARİANPOUR Kastamonu Üniversitesi, Türkiye
F. Kazemi
Hamıd Reza Rezaie
A. Asjodi
J. Liu
| Makale Türü | Özgün Makale (Diğer hakemli uluslarası dergilerde yayınlanan tam makale) | ||
| Dergi Adı | DIFFUSION IN SOLIDS AND LIQUIDS VIII | ||
| Dergi ISSN | 1012-0386 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | EI: Engineering Index | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2013 |
| Cilt / Sayı / Sayfa | 334335 / 0 / 381– | DOI | 10.4028/www.scientific.net/DDF.334-335.381 |
| UAK Araştırma Alanları |
Seramik Malzemeler
|
||
| Özet |
| Zirconium carbide (ZrC) has extended application in many ceramic and metal matrix composites especially used for ultra high temperature conditions. The synthesis of zirconium carbide powder is costly and difficult because of its high refractoriness and chemically inert properties. In this research, the synthesis of zirconium carbide nanopowder at low temperature via carbothermal reduction route was investigated according to thermodynamic data. The starting materials were zirconium acetate and sucrose as zirconium and carbon sources, respectively. After preparation of different carbon/zirconium ratio containing precursors, the dried precursors were heat treated at 1400°C and vacuum atmosphere. Also the ZrC formation was followed by thermal analysis of the produced precursors. The phase evolutions and microstructural studies were carried out using X-ray diffraction and scanning electron microscopy. The … |