The investigation of mechanical properties of B4C-reinforced AlSi7 foams
Yazarlar (2)
Prof. Dr. Arif UZUN Kastamonu Üniversitesi, Türkiye
Mehmet Turker Gazi Üniversitesi, Türkiye
Makale Türü Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
Dergi Adı International Journal of Materials Research (Q3)
Dergi ISSN 1862-5282 Dergi Bilgileri (2015)
Makale Dili İngilizce Basım Tarihi 09-2015
Cilt / Sayı / Sayfa 106 / 9 / 970–977 DOI 10.3139/146.111257
UAK Araştırma Alanları
Mühendislik
Özet
In this study, the mechanical properties of B4C-reinforced AlSi7 foams produced by using a powder metallurgy method were investigated. For this purpose, Al foams containing B4C at various ratios (0, 2, 4 and 6 %) were prepared with dimensions of 30 × 30 × 14 mm and 110 × 15 × 14 mm for compression and bending tests. Both tests were performed at a 1 mm min-1 strain rate. According to the experimental results, the compressive stress of B4C-reinforced/unreinforced AlSi7 foams, whose relative densities were close to each other, for 10 % strain increased about 15% with the addition of B4C. Although energy absorption values of B4C-reinforced/unreinforced AlSi7 foams were in a complex correlation for 60 % strain, the amount of absorption energy increased with the increase in relative density and the amount of B4C. Bending strength increased due to strain hardening that occurs with the addition of B4C to AlSi7 foams. While maximum bending strength was 0.9 kN in unreinforced materials, it was ∼1.15 kN in 6 % B4C-reinforced AlSi7 foams. Thus, the bending strength of B4C-reinforced materials is higher by ∼ 28 %.
Anahtar Kelimeler
AlSi7 foam | B4C | Compressive behavior | Mechanical properties
Atıf Sayıları
Scopus 1
The investigation of mechanical properties of B4C-reinforced AlSi7 foams

Paylaş

İletişim
  • Kastamonu Üniversitesi Rektörlüğü, Kuzeykent Kampüsü, Merkez/Kastamonu
  • unis@kastamonu.edu.tr 03662801000
Sosyal Media
Talentsoft Yazılım Talent Yazılım
Tasarım ve Programlama #2025