Influence of Vacuum Gas Nitriding on Wear and Corrosion Behavior of a High Manganese Steel     
Yazarlar (2)
Dr. Öğr. Üyesi Cihangir Tevfik SEZGİN Dr. Öğr. Üyesi Cihangir Tevfik SEZGİN
Kastamonu Üniversitesi, Türkiye
Fatih Hayat
Karabük Üniversitesi, Türkiye
Devamını Göster
Özet
In this study, the wear and corrosion behavior of gas-nitrided high manganese steel (HMS) was investigated. Vacuum gas nitriding was carried out for surface treatment of HMS at 520 and 570 °C for 12, 18 and 24 h. The base metal contained α and ε martensite, while austenite was also observed in heat-treated base metal. Although all gas-nitrided samples contain Fe3N, Fe4N, γ, α and ε martensite, FeSi phase was only determined in N1-N6 samples. Expanded martensite and white layer (complex S phase) were observed in N1-N6 and N7-12, respectively. The gas-nitriding process significantly increased the surface hardness of HMS due to the iron nitride. Daimler-Benz Rockwell-C adhesion test shows that gas-nitriding HMS has sufficient adhesion behavior. The gas-nitriding process increases the wear and corrosion resistance of the HMS significantly.
Anahtar Kelimeler
corrosion | gas nitriding | high manganese steel | wear
Makale Türü Özgün Makale
Makale Alt Türü SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale
Dergi Adı Journal of Materials Engineering and Performance
Dergi ISSN 1059-9495 Wos Dergi Scopus Dergi
Dergi Tarandığı Indeksler SCI-Expanded
Dergi Grubu Q3
Makale Dili Türkçe
Basım Tarihi 01-2025
Sayı 1
Doi Numarası 10.1007/s11665-025-11599-3
Makale Linki https://doi.org/10.1007/s11665-025-11599-3
BM Sürdürülebilir Kalkınma Amaçları
Atıf Sayıları
Influence of Vacuum Gas Nitriding on Wear and Corrosion Behavior of a High Manganese Steel

Paylaş