Comparative analysis of Tb and Zn doping effects on the microstructural and mechanical properties of YBCO-123 and YBCO-358 superconductors
Yazarlar (7)
Prof. Dr. Özgür ÖZTÜRK Kastamonu Üniversitesi, Türkiye
Gülnur Güdücü
Kastamonu Üniversitesi
Kastamonu Üniversitesi
Doç. Dr. Elif AŞIKUZUN TOKEŞER Kastamonu Üniversitesi, Türkiye
Öğr. Gör. Dr. Sedat KURNAZ Kastamonu Üniversitesi, Türkiye
Dr. Öğr. Üyesi Turgay SEYDİOĞLU Kastamonu Üniversitesi, Türkiye
Prof. Dr. Gürcan Yıldırım Bolu Abant İzzet Baysal Üniversitesi, Türkiye
Prof. Dr. Serap Safran Ankara Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Cryogenics (Q2) | ||
| Dergi ISSN | 0011-2275 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 11-2025 |
| Cilt / Sayı / Sayfa | 152 / 104236 / 104236–0 | DOI | 10.1016/j.cryogenics.2025.104236 |
| Makale Linki | https://doi.org/10.1016/j.cryogenics.2025.104236 | ||
| UAK Araştırma Alanları |
Süper İletken Malzemeler
|
||
| Özet |
| In this study, the microstructural and mechanical properties of copper-based superconducting systems synthesized via the sol–gel method-namely Y1-xTbxBa2Cu3O7-δ, Y1Ba2Cu3-xZnxO7-δ, Y3-xTbxBa5Cu8O18-δ, and Y3Ba5Cu8-xZnxO18-δ were comparatively investigated to evaluate the effects of varying concentrations of terbium (Tb) and zinc (Zn) dopants on the structural integrity, crystal quality, and micromechanical strength of both Y1-xTbxBa2Cu3O7-δ and Y3-xTbxBa5Cu8O18-δ superconducting phases. X-ray diffraction (XRD) assessed crystal structure, phase purity, and dopant effects, while scanning electron microscopy (SEM) characterized particle size distribution, surface morphology, porosity, and potential phase separation. Vickers microhardness (Hv) testing quantified micromechanical behavior under varying dopant concentrations. Results show that Zn and Tb substitutions influence crystal … |
| Anahtar Kelimeler |
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| Google Scholar | 1 |