| In this work, the effect of the partial substitution of Sn for Cu on structural, electrical and magnetic properties in the superconducting ceramic glass Bi1.75Pb0.25Sr2Ca2Cu3-xSnxO10+y system (x = 0, 0.1, 0.5) has been examined. The structural characterization of samples produced by glass-ceramic technique were done by X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements. The electrical and magnetic properties were determined by resistance-temperature (R-T) measurement and magnetization-magnetic field measurement (M-H) in the low temperature by using vibrating sample magnetometer (VSM), respectively. From the results of R-T measurement, the value of critical temperature (Tcoffset) has been decreased from 98 K to 73 K with increasing Sn- concentration. The critical current density has also been decreased with increasing magnetic field intensity. It has been observed from M-H plots that it was decreased with increasing the value of temperature. We have observed from M-H curves that the area size of the hysteresis curve decreases with increasing the value of temperature. |
| Anahtar Kelimeler |
| BSCCO | Glass-ceramic | Superconductivity |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | CRYOGENICS |
| Dergi ISSN | 0011-2275 |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Makale Dili | İngilizce |
| Basım Tarihi | 12-2017 |
| Cilt No | 88 |
| Sayı | 1 |
| Sayfalar | 17 / 21 |
| Doi Numarası | 10.1016/j.cryogenics.2017.09.006 |
| Makale Linki | http://linkinghub.elsevier.com/retrieve/pii/S0011227517301960 |
| Atıf Sayıları | |
| WoS | 3 |
| SCOPUS | 2 |
| Google Scholar | 4 |