Effect of Fe-Ni Substitution in FeNiSiB Soft Magnetic Alloys Produced by Melt Spinning
Yazarlar (5)
Muhammed Fatih Kılıcarslan
Yasin Yılmaz
Bekir Akgül
Hakan Karataş
Doç. Dr. Can Doğan VURDU Kastamonu Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(ESCI dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | ADVANCES IN MATERIALS SCIENCE | ||
| Dergi ISSN | 2083-4799 Wos Dergi | ||
| Dergi Tarandığı Indeksler | Emerging Sources Citation Index | ||
| Makale Dili | İngilizce | Basım Tarihi | 12-2021 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 01-12-2021 |
| Cilt / Sayı / Sayfa | 21 / 4 / 79–89 | DOI | 10.2478/adms-2021-0026 |
| Makale Linki | http://dx.doi.org/10.2478/adms-2021-0026 | ||
| Özet |
| Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid solidification technique. The magnetic and structural properties of FeNiSiB alloys with soft magnetic properties were investigated by increasing the Fe ratio. X-ray diffraction analysis and SEM images shows that the produced alloy ribbons generally have an amorphous structure, together with also partially nanocrystalline regions. It was observed that the structure became much more amorphous together with increasing Fe content in the composition. Among the alloy ribbons, the highest saturation magnetization was obtained as 0.6 emu/g in the specimen with 50 wt.% Fe. In addition, the highest Curie temperature was observed in the sample containing 46 wt.% Fe. |
| Anahtar Kelimeler |
| Alloy design | Curie temperature | FeNiSiB alloys | melt spinning | saturation magnetization |