| Yazarlar |
Ayman M. S. Eisay
|
Doç. Dr. Aydın TÜRKYILMAZ
Kastamonu Üniversitesi, Türkiye |
| Özet |
| The effectiveness of composite materials with the addition of activated carbon produced from biomaterial with a new application on aluminum-based composite materials was investigated in this study. Activated carbon was produced from the peanut shells via the chemical activation method and the obtained activated carbon was mixed with aluminum and composite material. For the characterization of the composite material obtained, XRD and SEM–EDS optical photographs were assessed in the experimental process. According to Vickers Hardness and Dynamic Micro Hardness results, the sample with the hardness value of 2% AC added had the highest hardness value. The value of the elastic modulus was found to be 9.59GPa with an increase of 3.4 times compared to aluminum with 2% activated carbon addition. This increases with activated carbon quantity, and weakens the composite structure due to weak van der waals interaction with aluminum, which reduces hardness; therefore, the best ratio of the activated carbon reinforcement to the aluminum matrix was obtained at 2% activated carbon addition. |
| Anahtar Kelimeler |
| Activated carbon | Aluminum | Characterization | Composite materials | Peanut shell |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayımlanan tam makale |
| Dergi Adı | JOURNAL OF INORGANIC AND ORGANOMETALLIC POLYMERS AND MATERIALS |
| Dergi ISSN | 1574-1443 |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q2 |
| Makale Dili | İngilizce |
| Basım Tarihi | 10-2021 |
| Cilt No | 31 |
| Sayı | 10 |
| Sayfalar | 4025 / 4032 |
| Doi Numarası | 10.1007/s10904-021-02048-4 |
| Makale Linki | http://dx.doi.org/10.1007/s10904-021-02048-4 |
| Atıf Sayıları | |
| WoS | 1 |
| SCOPUS | 1 |