WEAR CHARACTERISTICS OF FeW/FeW-B4C COATINGS PRODUCED BY TIG PROCESS
Yazarlar (1)
Prof. Dr. Serkan ISLAK Kastamonu Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | Archives of Metallurgy and Materials (Q4) | ||
| Dergi ISSN | 1733-3490 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 12-2017 |
| Cilt / Sayı / Sayfa | 62 / 4 / 2001–2006 | DOI | 10.1515/amm-2017-0298 |
| Makale Linki | https://yadda.icm.edu.pl/baztech/element/bwmeta1.element.baztech-33e8b32a-517b-4265-b466-2624a707280d | ||
| Özet |
| In this study, wear properties of FeW-B4C coatings produced by tungsten inert gas (TIG) process on the AISI 1060 steel were investigated. TIG process was selected because it is a cost-effective approach for melting-based coatings. The treated surfaces were evaluated and characterized by means of scanning electron microscope (SEM), X-ray diffraction analysis, and electron dispersive spectrometry (EDS). The microhardness and wear experiment were also performed by using a microhardness machine and ball-ondisk tribometer. SEM observations showed that the obtained coating had a smooth and uniform surface. According to XRD analysis, borides and carbides phases formed in the coatings. The wear behavior of the coatings was compared with ball-on-disc configuration wear tests, at the same conditions. Average coefficient of friction values of the coatings were obtained at relatively low levels. |
| Anahtar Kelimeler |
| coating | microstructure | TIG process | Wear |